Research and development of specific surface area standard reference materials of nonporous mono-disperse SiO<sub>2</sub> spheres

ZHANG Yimei; ZHOU Qian; CHEN Shengli; DONG Peng; YUAN Guimei

您当前的位置：

首页 >

文章列表页 >

Research and development of specific surface area standard reference materials of nonporous mono-disperse SiO₂ spheres

更新时间：2025-12-10

- Research and development of specific surface area standard reference materials of nonporous mono-disperse SiO₂ spheres
- CIESC Journal Issue 5, Pages: 1327-1331(2009)
- 作者机构：
  
  中国石油大学重质油国家重点实验室
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Online First：05 May 2009，
  
  Published：05 May 2009
- 稿件说明：
移动端阅览
ZHANG Yimei, ZHOU Qian, CHEN Shengli, et al. Research and development of specific surface area standard reference materials of nonporous mono-disperse SiO₂ spheres[J]. CIESC Journal, 2009, (5): 1327-1331.
DOI：

ZHANG Yimei, ZHOU Qian, CHEN Shengli, et al. Research and development of specific surface area standard reference materials of nonporous mono-disperse SiO₂ spheres[J]. CIESC Journal, 2009, (5): 1327-1331. DOI：

摘要

提出一种新型比表面积标准物质的研究思路，即用无孔的单分散SiO2微球作为比表面积标准物质的材料，它的“真实”比表面积可以通过对其粒径的准确测量，用几何的方法计算出来。这种比表面积标准物质的研制首先要进行单分散SiO2微球的批量合成；其次是对SiO2微球进行表面修饰使其表面无孔；再次是对封孔后SiO2微球的特征尺寸（如粒径、密度）进行测定；最后是进行比表面积的计算和BET测定。实验结果表明：经1000℃灼烧 3h可使SiO2微球基本不含微孔。采用BET法测量的BET比表面积比它的理论计算比表面积值大，粒径为1150nm、453nm和269nm的SiO2微球的BET比表面积比它们的理论计算比表面积分别大1.2m2·g-1、 2.0 m2·g-1和3.6 m2·g-1。在这种情况下，计算比表面积值可以作为这类标准物质定值的参考数据。

Abstract

A new idea for specific surface area standard reference materials (SRM) which are made of nonporous mono-disperse SiO2 spheres and the true specific surface area can be calculated accurately from their diameters is presented.Firstly

the mono-disperse SiO2 spheres were synthesized in bulk.Secondly

the spheres were modified to make them nonporous.Thirdly

the characteristic dimensions

such as the size

density of the spheres

were determined accurately.Finally

the specific surface areas were measured by using a static volumetric type Brunauer-Emmett-Teller (BET) (nitrogen gas) instrument.The experimental results showed that the micro-holes on the surface of mono-disperse SiO2 spheres were almost be sealed by calcining at the temperature of 1000℃ for three hours.The BET surface area was larger than the geometric specific surface area and the values of the deviation were 1.2 m2·g-1

2.0 m2·g-1 and 3.6 m2·g-1 for mono-disperse SiO2 spheres with diameters 1150 nm

453 nm and 269 nm respectively.In this case

the theoretical value can be used as reference for the determination of the specific surface area of nonporous mono-disperse SiO2 spheres SRMs.

关键词

Keywords

references

Views

722

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

EFFECTS OF POROSITY AND SURFACE PROPERTIES OF POLYMERIC RESINS ON ADSORPTION CAPACITY OF PHENOL

Construction of transition metal-based nitrogen-doped carbon and their desulfurization performance

Performance study of gas-liquid vortex separators under low cross-sectional gas velocity

Thermo-gas-elastic coupling performance analysis of high-speed and high-temperature foil face seals

Study on performance enhancement and cold retention characteristics of solid packed bed cold energy storage

Related Author

WU Yongwen

LI Zhong

XI Hongxia

LI Xiangbin

HAN Jinglei

GUO Jianguang

Related Institution

华南理工大学化学工程研究所

⁰

Research and development of specific surface area standard reference materials of nonporous mono-disperse SiO2 spheres

DOI：

摘要

Abstract

关键词

Keywords

references

Research and development of specific surface area standard reference materials of nonporous mono-disperse SiO₂ spheres