Preparation of PVA/SA composite hydrogel and its diffusibility performance for NH+4，NO-2 and NO-3

LAI Zini; CUI Yingde; WU Xingxiang

您当前的位置：

首页 >

文章列表页 >

Preparation of PVA/SA composite hydrogel and its diffusibility performance for NH⁺₄，NO^-₂ and NO^-₃

更新时间：2025-12-10

- Preparation of PVA/SA composite hydrogel and its diffusibility performance for NH⁺₄，NO^-₂ and NO^-₃
- CIESC Journal Issue 12, Pages: 3144-3149(2008)
- 作者机构：
  
  1. 西北工业大学材料学院,陕西,西安,710072
  2. 中国水产科学院珠江水产研究所,广东,广州,510380
  3. 仲恺农业工程学院化学与化工系,广东,广州,510225
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Online First：05 December 2008，
  
  Published：05 December 2008
- 稿件说明：
移动端阅览
LAI Zini, CUI Yingde, WU Xingxiang. Preparation of PVA/SA composite hydrogel and its diffusibility performance for NH⁺₄，NO^-₂ and NO^-₃[J]. CIESC Journal, 2008, (12): 3144-3149.
DOI：

LAI Zini, CUI Yingde, WU Xingxiang. Preparation of PVA/SA composite hydrogel and its diffusibility performance for NH⁺₄，NO^-₂ and NO^-₃[J]. CIESC Journal, 2008, (12): 3144-3149. DOI：

摘要

以聚乙烯醇（PVA）、海藻酸钠（SA）、活性炭、硼酸和氯化钙为原料，制备复合水凝胶微生物固定化载体材料，分析了离子在水凝胶膜中的扩散渗透机理，采用池膜法测定水凝胶的NH+4、NO-2、NO-3离子扩散性能。结果表明，在PVA、SA、活性炭含量分别为4％、2.0%及0.2%时，以5%的氯化钙的饱和硼酸溶液为交联剂，交联时间15 min的条件下制备的固定化脱氮微生物载体传递性能最佳。复合水凝胶平衡溶胀度、扩散系数随PVA浓度升高而增大，随SA浓度升高溶胀度降低，离子扩散系数起初随SA浓度升高而升高，随后出现拐点。3种无机氮离子在水凝胶中的传递速率依次为NH+4>NO-2>NO-3，遵从离子有效截面积小，传递速率大的规律。改变水凝胶制备条件、原料配比对NO-2、NH+4的渗透系数影响较大，而对NO-3影响较小。

Abstract

A copolymer hydrogel for immobilized microorganism carrier was synthesized by using sodium alginate（SA），polyvinyl alcohol（PVA）and active carbon as start materials and calcium chloride and boric acid as crosslinker.The ionic diffusion mechanism was analyzed and the diffusibility of NH+4，NO-2 and NO-3 was measured by the static penetration method.The result showed that the hydrogel prepared by crosslink 4% PVA，2.0% sodium alginate and 0.2% active carbon with 5% calcium chloride and saturated boric acid as crosslinker for 15 min possessed the highest ionic permeability.The degree of equilibrium swelling and ionic diffusion coefficient of the composite hydrogel increased with increasing concentration of PVA.The degree of equilibrium swelling decreased with increasing concentration of SA but the ionic diffusion coefficient first increased and then decreased with increasing SA concentration.The diffusion rate of the inorganic nitrogen-containing ion in the hydrogel decreased as fellows：NH+4> NO-2> NO-3.The synthesis condition and the start materials ratio had a great impact on the diffusion coefficient of NO-2 and NH+4，but a relatively small impact on that of NO-3.

关键词

Keywords

references

Views

259

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

In-situ visual measurement of poly(methyl methacrylate) swelling in supercritical carbon dioxide and interrelated thermodynamic modeling

Study on impact of impurities in coal chemical waste salt on solvation of NaCl and Na2SO4

New universal corresponding state equation for correlation and extrapolation of saturated vapor-liquid density

Study on the residence time distribution characteristics of the TPMS-Diamond static mixer

Study on microstructure of NaCl solution ice centrifugal separation based on Micro-CT and deep learning

Related Author

CHEN Lihua

CAO Guiping

ZHANG Renhan

HE Feng

LIU Tao

ZHAO Ling

YUAN Weikang

George W.Roberts

Related Institution

华东理工大学联合化学反应工程研究所，化学工程联合国家重点实验室

Department of Chemical and Biomolecular Engineering, North Carolina State University

⁰