无烟粉煤催化气化含碱灰渣的煅烧脱碱

LI Baoxia; ZHANG Jiyu

您当前的位置：

首页 >

文章列表页 >

无烟粉煤催化气化含碱灰渣的煅烧脱碱

更新时间：2025-12-10

- 无烟粉煤催化气化含碱灰渣的煅烧脱碱
- CIESC Journal Issue 11, (2006)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Online First：25 November 2006，
  
  Published：25 November 2006
- 稿件说明：
移动端阅览
LI Baoxia, ZHANG Jiyu. 无烟粉煤催化气化含碱灰渣的煅烧脱碱[J]. CIESC Journal, 2006, (11).
DOI：

LI Baoxia, ZHANG Jiyu. 无烟粉煤催化气化含碱灰渣的煅烧脱碱[J]. CIESC Journal, 2006, (11). DOI：

摘要

在具有温控的小型高温加热炉中，通过静态煅烧研究了温度、时间及助剂对高变质程度无烟粉煤催化气化后的含碱灰渣中碱含量的影响，结果表明：最佳的脱碱煅烧温度及时间分别为870℃和30 min;最佳的脱碱助剂高岭土在其添加浓度为5％时，灰渣脱碱率可达100％.采用X射线粉晶衍射及扫描电镜对煅烧后的灰渣进行表征，揭示了含碱灰渣煅烧脱碱过程的实质，即在适宜煅烧温度下，含碱灰渣中被活化的主要矿物质SiO2（形成玻璃网络氧化物）、Al2O3（修饰中间氧化物）和熔融并分解的Na2CO3（分解为修饰网络氧化物Na2O）等发生化学反应转变为中性物质霞石（NaAlSiO4）及其他无定形复合硅酸盐，从而降低了灰渣中的碱含量.

Abstract

The effects of calcination temperature

time and additives on the alkali content of coal-cinder from the catalytic gasification of pulverized anthracite were examined by using the static calcination method in a laboratory high temperature furnace in this study.The results indicated that the optimum calcination temperature and time were respectively 870℃and 30 min

and the optimum dealkalization additive is kaolinite.By adding only 5% kaolinite in the calcination process

the dealkalization rate could be increased to 100%.Most importantly

with analyzing the calcined cinder by X-ray powder diffraction (XRD) and scanning electron microscope(SEM)

it was clear that at an appropriate calcination temperature

the activated SiO2 and Al2O3 in alkaline coal-cinder would react with the decomposed fused Na2CO3 to form a new neutral matter nepheline（NaAlSiO4）and other amorphous silicate compounds

causing an obvious reduction of the alkali content in coal-cinder.

关键词

Keywords

references

Views

314

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Effect of belt structure design on the vulcanization characteristics of all-steel radial tires

Prediction of biomass pyrolysis product yield based on machine learning algorithms

Identification of gas-liquid two-phase flow patterns in a riser based on recursive characteristics and CNN

Thermo-oxidative degradation characteristics of TPT backsheet from end-of-life photovoltaic modules

Zn-doped PdO/ZrO2 with rich oxygen vacancies for the synthesis of diphenyl carbonate from CO2 and phenol

Related Author

No data

Related Institution

No data

⁰