Preparation of epoxide-acrylate-polyurethane hybrid dispersions

傅和青 黄洪 张心亚 陈焕钦

您当前的位置：

首页 >

文章列表页 >

Preparation of epoxide-acrylate-polyurethane hybrid dispersions

更新时间：2025-12-10

- Preparation of epoxide-acrylate-polyurethane hybrid dispersions
- CIESC Journal Issue 2, (2007)
- 作者机构：
  
  广东省广州市华南理工大学化工与能源学院华南理工大学化工学院化工所华南理工大学化工学院化工所华南理工大学化工学院化工研究所
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Online First：05 February 2007，
  
  Published：05 February 2007
- 稿件说明：
移动端阅览
傅和青黄洪张心亚陈焕钦. Preparation of epoxide-acrylate-polyurethane hybrid dispersions[J]. CIESC Journal, 2007, (2).
DOI：

傅和青黄洪张心亚陈焕钦. Preparation of epoxide-acrylate-polyurethane hybrid dispersions[J]. CIESC Journal, 2007, (2). DOI：

摘要

以三羟甲基丙烷（TMP）为交联剂，先用环氧树脂改性聚氨酯（PU），得到环氧树脂改性的水性聚氨酯（WPUE）分散体，然后加入甲基丙烯酸甲酯（MMA）和引发剂偶氮二异丁腈（AIBN），通过自由基乳液聚合得到聚氨酯-环氧树脂-丙烯酸酯（WPUEA）杂合分散体，并通过傅里叶红外光谱、凝胶渗透色谱、粒径分析仪和透射电镜对其进行了表征。研究了－NCO/OH总摩尔比、交联剂TMP的量、环氧树脂种类和量、MMA的量等对WPUEA杂合分散体性能以及涂膜性能的影响。实验结果表明，选用E20环氧树脂，当－NCO/OH总摩尔比为12～15， TMP的添加量为4%～8％，E20添加量为4％～6％，MMA添加量为10%～30%时得到WPUEA杂合分散体性能较佳，所得到的水性WPUEA杂合分散体的涂膜硬度为073，光泽度达到85，表干时间为30min，冻融循环大于5，同时耐水性和耐溶剂性均得到提高。该产品可以取代溶剂型产品。

Abstract

The aqueous polyurethane modified by epoxide resin(WPUE) was prepared with trimethylolpropane(TMP) as cross linker

then epoxide-acrylate-polyurethane(WPUEA) hybrid dispersions were synthesized by free-radical emulsion polymerization which were carried out by using azodiisobutyronitrile (AIBN) as initiator and methyl methacrylate (MMA) as monomerThe WPUEA hybrid dispersions were characterized with FT-IR

gel permeation chromatography (GPC)

Malvern particle size analyzer and TEMThe influences of the total mole ratio of NCO/OH

the type and amount of epoxide resin

the amounts of TMP and MMA on the properties of the hybrid dispersions and the coating films were studiedThe experimental results showed the WPUEA hybrid emulsions had better properties at total mole ratio of-NCO/OH 12—15

TMP 4%—8％

E20 4％—6％

MMA 10%—30%At the same time

the coating films of WPUEA showed such better properties as:hardness 073

gloss 85

surface drying time 30 min

freezing and thawing cycle above 5The water resistance and solvent resistance of the films of WPUEA were improvedThe modified WPUEA hybrid emulsions could substitute for solvent polyurethane.

关键词

Keywords

references

Views

721

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Performance study of gas-liquid vortex separators under low cross-sectional gas velocity

Advantages and risks of swirling cooling granulation towers

Methods of adaptive prediction and abnormal states traceability for sulphur content in flue gas desulfurization process

Prediction of biomass pyrolysis product yield based on machine learning algorithms

Thermal analysis of phase change suspension jet impinging on wall surface covered with variable-shape porous layer

Related Author

No data

Related Institution

No data

⁰