Copolymerization of dimethyl diallyl ammonium chloride and acrylamide by using AIBA·2HCl-NaHSO<sub>3</sub> initiator and characterization

ZHANG Wanzhong; QIAO Xueliang; CHEN Jianguo; LI Miangui

您当前的位置：

首页 >

文章列表页 >

Copolymerization of dimethyl diallyl ammonium chloride and acrylamide by using AIBA·2HCl-NaHSO₃ initiator and characterization

更新时间：2025-12-10

- Copolymerization of dimethyl diallyl ammonium chloride and acrylamide by using AIBA·2HCl-NaHSO₃ initiator and characterization
- CIESC Journal Issue 10, Pages: 1998-2003(2005)
- 作者机构：
  
  1. 模具技术国家重点实验室，华中科技大学材料学院,湖北,武汉,430074
  2. 湖北省化学研究所,湖北,武汉,430074
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Online First：25 October 2005，
  
  Published：25 October 2005
- 稿件说明：
移动端阅览
ZHANG Wanzhong, QIAO Xueliang, CHEN Jianguo, et al. Copolymerization of dimethyl diallyl ammonium chloride and acrylamide by using AIBA·2HCl-NaHSO₃ initiator and characterization[J]. CIESC Journal, 2005, (10): 1998-2003.
DOI：

ZHANG Wanzhong, QIAO Xueliang, CHEN Jianguo, et al. Copolymerization of dimethyl diallyl ammonium chloride and acrylamide by using AIBA·2HCl-NaHSO₃ initiator and characterization[J]. CIESC Journal, 2005, (10): 1998-2003. DOI：

摘要

采用偶氮二异丁脒二盐酸盐(AIBA·2HCl)和NaHSO3(RH)组成的引发体系，研究了引发剂浓度、溶液的pH值、引发剂复配和加料方式等因素对二甲基二烯丙基氯化铵(DMDAAC)-丙烯酰胺(AM)共聚合反应规律的影响.结果表明：在30 ℃、nAM∶nDMDAAC=4∶1、ω(monomer) =30％和引发剂AIBA·2HCl-RH的浓度为1.0×10-4 mol·L-1的条件下， pH=7.0时， DMDAAC-AM共聚物的特性黏数达11.56 dl·g-1;pH=10.0时，特性黏数最高达13.60 dl·g-1.采取连续加料方式，可获得阳离子度38.8％，特性黏数达11.61 dl·g-1的共聚物.进一步测得该引发体系30 ℃下，聚合反应的表观活化能为33.25 kJ·mol-1，单体的竞聚率为γAM=6.800，γDMDAAC=0.174.

Abstract

By using AIBA·2HCl-NaHSO3 initiation system，a series of high intrinsic viscosity copolymers of dimethyl diallyl ammonium chloride(DMDAAC) and acrylamide(AM) were prepared in aqueous medium under different conditions.The effects of various factors such as initiator concentration

pH of solution

composite initiator and the way of feeding AM etc.on the copolymerization of dimethyl diallyl ammonium chloride and acrylamide were studied. The results indicated that copolymerization could be initiated at a low temperature.At 30℃

nAM∶nDMDAAC=4∶1

ω(monomer)=30％

c(AIBA·2HCl)=1.0×10-4 mol·L-1，when the monomer solution was polymerized at pH=7.0，the intrinsic viscosity of PDMDAAC-AM was 11.56 dl·g-1;when the monomer solution was polymerized at pH=10.0，the intrinsic viscosity of copolymer was up to 13.60 dl·g-1.If continuous feeding of AM was used

the cationicity and intrinsic viscosity of copolymer could attain 38.8％ and 11.61 dl·g-1.Furthermore

the monomer reactivity ratios and apparent activation energy of the polymerization system were determined.

关键词

Keywords

references

Views

651

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Preparation of titanium dioxide nanotube and its catalytic activity for ozonation

APPARENT ACTIVATION ENERGY OF PYROLYSIS REACTION OF COPOLYMERS OF ACRYLONITRILE AND N-VINYLPYRROLIDONE

Zn-doped PdO/ZrO2 with rich oxygen vacancies for the synthesis of diphenyl carbonate from CO2 and phenol

Oxygen mass transfer performance of hollow fiber non-bubble aeration membrane based on gas/liquid-phase measurement method

Recent advances and perspectives on sulfide-based photocatalysts for hydrogen production

Related Author

PAN Liuming

JI Min

WANG Miaomiao

ZHANG Xin

LU Bin

CHEN Hou

WANG Chengguo

CAI Huasu

Related Institution

天津大学环境科学与工程学院

山东大学材料科学与工程学院

⁰

Copolymerization of dimethyl diallyl ammonium chloride and acrylamide by using AIBA·2HCl-NaHSO3 initiator and characterization

DOI：

摘要

Abstract

关键词

Keywords

references

Copolymerization of dimethyl diallyl ammonium chloride and acrylamide by using AIBA·2HCl-NaHSO₃ initiator and characterization