Tetrahydrofuran polymerization catalyzed by organic-inorganic hybrid clay

更新时间：2025-12-10

- Tetrahydrofuran polymerization catalyzed by organic-inorganic hybrid clay
- CIESC Journal Issue 7, Pages: 1673-1679(2009)
- 作者机构：
  
  1. 山西大学化学化工学院，精细化学品教育部工程研究中心
  2. 山西三维集团股份有限公司
  3. 北京化工大学化工资源有效利用国家重点实验室
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Online First：05 July 2009，
  
  Published：05 July 2009
- 稿件说明：
移动端阅览
WANG Pengfei, JIA Zhiqi, ZHAO Min, et al. Tetrahydrofuran polymerization catalyzed by organic-inorganic hybrid clay[J]. CIESC Journal, 2009, (7): 1673-1679.
DOI：

WANG Pengfei, JIA Zhiqi, ZHAO Min, et al. Tetrahydrofuran polymerization catalyzed by organic-inorganic hybrid clay[J]. CIESC Journal, 2009, (7): 1673-1679. DOI：

摘要

采用后合成方法，将γ-巯基丙基三乙氧基硅烷嫁接到黏土表面，获得含磺酸有机功能团的黏土固体酸催化剂。经XRD、N2 吸附-脱附、FTIR、吡啶吸附和酸量滴定等物性结构表征及催化四氢呋喃聚合的反应活性评价，结果表明，改性后的黏土保持了原有黏土介孔结构，孔径分布集中在3 ～4.3 nm，酸量增加了35％，在催化四氢呋喃聚合反应中显现出较高的催化活性，在反应温度为35℃、反应时间为8 h的条件下，聚合产物收率达30％，得到数均分子量为2000左右、可用作氨纶生产原料的聚合物。

Abstract

A kind of solid acid catalyst containing alkyl sulfonic acid group was prepared by post-synthesis grafting of 3-mercaptopropyltriethoxysilane (MPTES) to the surface of acid-modified clay.The clay samples were characterized by means of XRD

N2 adsorption-desorption

FTIR

IR analysis of adsorbed pyridine and acid-base titration.The results showed that the hybrid material maintained the mesoporous structure with pore size mainly distributed in 3－4.3 nm

and the acid amount increased by 35%.In the polymerization of tetrahydrofuran

the organic-inorganic hybrid clay catalyst showed good catalytic performance.When the temperature was 35℃ and the reaction time was 8 h

the yield of polymer reached 30% and the number-average molecular weight was about 2000.

关键词

Keywords

references

Views

256

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Kinetics of styrene reversible addition-fragmentation chain transfer polymerization

Preparation, polymerization of reverse microemulsion of acrylamide and its micro-structure

Non-equilibrium stage simulation of hydrate separation for H2+CH4

New universal corresponding state equation for correlation and extrapolation of saturated vapor-liquid density

Methods of adaptive prediction and abnormal states traceability for sulphur content in flue gas desulfurization process

Related Author

WANG Zhenxi

ZHANG Qinghua

ZHAN Xiaoli

CHEN Fengqiu

XIONG Jihai

WANG Fenghe

LU Shi

LEI Wu

Related Institution

浙江大学化学工程与生物工程学系

江西省科学院能源研究所

南京理工大学化工学院

石油大学流体高压相态及物性研究实验室

⁰