Hydrolysis resistance of aluminum nitride powder modified by organic carboxylic acid

GUO Xingzhong; YANG Hui; ZHANG Lingjie; MA Qi; GAO Lihua; FU Peixin

您当前的位置：

首页 >

文章列表页 >

Hydrolysis resistance of aluminum nitride powder modified by organic carboxylic acid

更新时间：2025-12-10

- Hydrolysis resistance of aluminum nitride powder modified by organic carboxylic acid
- CIESC Journal Issue 9, Pages: 2412-2415(2008)
- 作者机构：
  
  1. 浙江大学材料科学与工程学系
  2. 浙江东新密封有限公司
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Online First：05 September 2008，
  
  Published：05 September 2008
- 稿件说明：
移动端阅览
GUO Xingzhong, YANG Hui, ZHANG Lingjie, et al. Hydrolysis resistance of aluminum nitride powder modified by organic carboxylic acid[J]. CIESC Journal, 2008, (9): 2412-2415.
DOI：

GUO Xingzhong, YANG Hui, ZHANG Lingjie, et al. Hydrolysis resistance of aluminum nitride powder modified by organic carboxylic acid[J]. CIESC Journal, 2008, (9): 2412-2415. DOI：

摘要

采用有机羧酸和PEG作为表面活性剂对工业AlN粉体进行表面改性处理，研究了改性前后AlN粉体的抗水解特性以及表面改性机制。研究结果表明，AlN表面与水分子发生化学反应，导致溶液的pH值迅速提高，表面包覆有机羧酸可有效地改善AlN粉体的抗水解性能；AlN粉体在水中浸泡48h后，氮含量基本保持不变，除了AlN晶相外，没有其他晶相出现，且改性粉体在高剪切应力的水基球磨介质中也保持较强的稳定性。

Abstract

Industrial aluminum nitride(AlN) powder was surface modified with organic carboxylic acid and polyethylene glycol (PEG) as surface modifier and the hydrolysis resistance and modifying mechanism of AlN powder before and after modification were studied.The results showed that the hydrolysis reaction to produce NH3 between AlN and H2O led to the rapid increase of pH value of aqueous solution and generation of much Al(OH)3.The surface coating organic carboxylic acid on AlN particles formed a diffusion barrier between water and AlN surface to improve the hydrolysis resistance of AlN. The pH value of AlN powder after modification slightly increased after soaking in water for 48h

but there was no obvious Al(OH)3 generation.The AlN powder after modification kept higher stability in aqueous ball milling at a high cutting stress.

关键词

Keywords

references

Views

734

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Effect of modified nanoTiO2 on properties of coating and coated paper

Surface modification of graphite/phenolic resin composite plates with expanded graphite for PEMFC

EXTRACTION EQUILIBRIUM CHARACTERISTICS OF DICARBOXYLIC ACIDS WITH TRIALKYLPHOSPHINE OXIDE AS EXTRACTANT AND 1-OCTANOL AS DILUENT

Progress in research of selective oxidation of low carbon polyols over nano-Au catalysts with precise electronic effect regulation

Identification of gas-liquid two-phase flow patterns in a riser based on recursive characteristics and CNN

Related Author

LI Bin

LI Youming

LU Ruijiang

LI Dongjie

LU Jun

WANG Yuxin

LI Yuxin

WANG Yundong

Related Institution

华南理工大学制浆造纸工程国家重点实验室

华南理工大学造纸与污染控制国家工程研究中心

天津大学化工学院化学工程研究所，化学工程联合国家重点实验室

清华大学化学工程联合国家重点实验室

⁰