Preparation and properties of polylactic acid/silk fibroin blend membrane

CHEN Jianyong; ZHANG Jiazhong; FENG Xinxing; ZHU Hailin; ZHENG Guifen; WANG Yongjun

您当前的位置：

首页 >

文章列表页 >

Preparation and properties of polylactic acid/silk fibroin blend membrane

更新时间：2025-12-10

- Preparation and properties of polylactic acid/silk fibroin blend membrane
- CIESC Journal Issue 3, Pages: 773-777(2008)
- 作者机构：
  
  浙江理工大学“先进纺织材料与制备技术”教育部重点实验室，材料与纺织学院
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Online First：05 March 2008，
  
  Published：05 March 2008
- 稿件说明：
移动端阅览
CHEN Jianyong, ZHANG Jiazhong, FENG Xinxing, et al. Preparation and properties of polylactic acid/silk fibroin blend membrane[J]. CIESC Journal, 2008, (3): 773-777.
DOI：

CHEN Jianyong, ZHANG Jiazhong, FENG Xinxing, et al. Preparation and properties of polylactic acid/silk fibroin blend membrane[J]. CIESC Journal, 2008, (3): 773-777. DOI：

摘要

用分子量为10万的聚乳酸（PLLA）对丝素膜进行改性，研究不同的聚乳酸加入量对丝素膜性能的影响，对聚乳酸/丝素共混膜进行了一系列表征。万能电子试验机的测试结果表明，经聚乳酸改性后，丝素膜的断裂强度，断裂伸长率有了较大的改善，当加入聚乳酸占丝素质量为5%时，丝素膜的强度可达到27.1 MPa，伸长率达4.4%; 改性后的丝素膜的亲水性有一定程度降低，溶失率则明显减小，透汽透湿性也有所提高；红外光谱测试表明，改性后的丝素膜含有较多的β构象成分。

Abstract

The blend membranes of regenerated SF (silk fibroin) / polylactic acid (PLLA) with molecular weight 100000 were prepared by using different ratios of SF and polylactic acid

and the effects of polylactic acid on silk fibroin were studied.The structures and properties of these membranes were characterized by a series of tests.Through an electronic mechanical testing system

it was demonstrated that the tensile strength and elongation at break of the blend membrane were improved greatly.When the mass percentage of PLLA reached 5%

tensile strength could reach 27.1 MPa

and elongation at break could reach 4.4%.The hydrophilicity of the blend membrane decreased

and its solubility was reduced evidently

but its water permeability increased.The FTIR measurement indicated that the amount of β-sheet structures of the blend membrane was greater than the pure membrane.

关键词

Keywords

references

Views

225

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

LiFePO4 synthesized by hydrothermal method from Li3PO4 and its modification

Alkylation of benzene with 1-butylene over β-zeolite modified by Fe or La

Modification of carbon black produced from pyrolysis of scrap tires

Structure and antibacterial ability of in situ silver-modified hexagonal mesoporous silica

Modification of ricinine and insecticidal effect on Aedes albopictus Skuse

Related Author

ZHANG Weixin

ZHAO Fei

WANG Qiang

YANG Zeheng

HUANG Xinjiang

FU Kaimei

HU Yaochi

ZOU Bin

Related Institution

合肥工业大学化工学院, 可控化学与材料化工安徽省重点实验室

南京工业大学材料化学工程国家重点实验室

南开大学环境科学与工程学院

南京林业大学化工学院

安徽科技学院化学系

⁰