Preparation, polymerization of reverse microemulsion of acrylamide and its micro-structure

更新时间：2025-12-10

- Preparation, polymerization of reverse microemulsion of acrylamide and its micro-structure
- CIESC Journal Issue 6, Pages: 1447-1452(2006)
- 作者机构：
  
  南京理工大学化工学院,江苏,南京,210094
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Online First：25 June 2006，
  
  Published：25 June 2006
- 稿件说明：
移动端阅览
WANG Fenghe, LU Shi, LEI Wu, et al. Preparation, polymerization of reverse microemulsion of acrylamide and its micro-structure[J]. CIESC Journal, 2006, (6): 1447-1452.
DOI：

WANG Fenghe, LU Shi, LEI Wu, et al. Preparation, polymerization of reverse microemulsion of acrylamide and its micro-structure[J]. CIESC Journal, 2006, (6): 1447-1452. DOI：

摘要

制备稳定的Span80-Tween80/异辛烷/AM-H2O反相微乳液聚合体系;用电导法考察了不同HLB（亲水-亲油平衡）值下电导率的变化规律;研究了正丁醇、氯化钠和乙酸钠对微乳液体系电导率变化的影响规律.采用TEM、AFM、DSC、激光纳米粒度仪等手段测定了聚合前后微乳液的粒子形态、粒度和粒度分布.结果表明：HLB为5.4时，体系的电导率变化较小，正丁醇浓度为25 g8226;L-1时电导率几乎没有变化，形成的微乳液较为稳定，而且增溶的水相也比较多.当氯化钠浓度为50 g8226;L-1或醋酸钠浓度为25 g8226;L-1时会增加体系的稳定性.对该体系聚合，可以得到相对分子质量（MR）为5.64×106、固含量为32%的聚合物乳液.所制备的聚合物为球形、单分散的准纳米材料，粒径（D）在140 nm左右.反相微乳液聚合的聚丙烯酰胺（PAM）的比表面积为21.684 m28226;g-1，玻璃化转变温度Tg为193℃.

Abstract

The reverse microemulsion of Span80-Tween80/isooctane/AM-H2O was prepared and polymerized

and the regular changes of electrical conductance at different HLB values were studied with the conductivity method.The effects of adding n-butanol

NaCl and NaAc on the changes of conductivity properties were discussed.The micro-structure and the size distribution of PAM particle were invested with TEM

AFM

DSC

laser nanometer measurement before and after polymerization.The results showed that the change of electrical conductance was lower when HLB value approached 5.4

it almost had no change when the concentration of n-butanol was 25 g8226;L-1

and its stability was enhanced when 50 g8226;L-1 NaCl or 25 g8226;L-1 NaAc was added in the system.Polymer microemulsion relative molecule weight（MR）5.64×106 and solid content of PAM 32% was obtained after polymerization

and the polymer was mono-disperse

globular nanometer material.The diameter of PAM particle(D) was 140 nm

and its size distribution was narrow.The surface area and glass transformation temperature (Tg) of the polymer was 21.684 m28226;g-1 and 193℃

respectively.

关键词

Keywords

references

Views

245

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

KLPAAM复合高吸水树脂吸附

Influence of intercalated anions on electrochemical performance of Al substituted nickel hydroxide

Kinetics of styrene reversible addition-fragmentation chain transfer polymerization

Capturing sulphur behavior of calcium-based industrial waste at fluidized bed boiler temperature

Property and microstructure of ABS composite modified with salt sulfate whisker

Related Author

吴义强

韩心强

张绘营

谢建军

何新建

LI Yanwei

LI Yuexiao

YAO Jinhuan

Related Institution

中南林业科技大学材料科学与工程学院

桂林理工大学有色金属及材料加工新技术教育部重点实验室

桂林理工大学化学与生物工程学院

江西省科学院能源研究所

浙江大学化学工程与生物工程学系

⁰