Preparation and characterization of 3,4,5-trimethoxybenzoyl-3,5-dimethylbenzoylchitin

DUO Yingquan; CHEN Yu; LUO Yunjun; TAN Huimin

您当前的位置：

首页 >

文章列表页 >

Preparation and characterization of 3,4,5-trimethoxybenzoyl-3,5-dimethylbenzoylchitin

更新时间：2025-12-10

- Preparation and characterization of 3,4,5-trimethoxybenzoyl-3,5-dimethylbenzoylchitin
- CIESC Journal Issue 10, Pages: 2014-2018(2005)
- 作者机构：
  
  北京理工大学材料科学与工程学院,北京,100081
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Online First：25 October 2005，
  
  Published：25 October 2005
- 稿件说明：
移动端阅览
DUO Yingquan, CHEN Yu, LUO Yunjun, et al. Preparation and characterization of 3,4,5-trimethoxybenzoyl-3,5-dimethylbenzoylchitin[J]. CIESC Journal, 2005, (10): 2014-2018.
DOI：

DUO Yingquan, CHEN Yu, LUO Yunjun, et al. Preparation and characterization of 3,4,5-trimethoxybenzoyl-3,5-dimethylbenzoylchitin[J]. CIESC Journal, 2005, (10): 2014-2018. DOI：

摘要

用共酰化方法制备了3

5-三甲氧基苯甲酰-3

5-二甲基苯甲酰甲壳素，获得了一类新型的具有良好溶解性能的高分子紫外线吸收剂.通过元素分析的数据计算了两种酰基的取代度，FTIR表征表明了取代反应的发生，采用X射线衍射和TG等手段对酰化产物的结晶性能和热稳定性进行了研究，通过紫外吸光度的测定计算出两种取代基的摩尔消光系数分别为9329.1 L8226;mol-18226;cm-1和652.7 L8226;mol-18226;cm-1，并对产物中的酰基进行了定量分析，结果与元素分析结果基本一致.

Abstract

5-trimethoxybenzoyl-3

5-dimethylbenzoylchitin

a kind of novel macromolecular UV absorbent with good solubility was prepared through the co-acidylating method.The substitution degree of two kinds of acyl group was calculated from the data of elemental analysis.The substitution reaction was demonstrated by the result of FTIR.The crystallinity and thermal stability of the products were studied with the methods of X-ray diffraction and TG. The molar absorptivity values of two kinds of acyl group were 9329.1 L8226;mol-18226;cm-1 and 652.7 L8226;mol-18226;cm-1 respectively

which were calculated from the data of UV absorbance.Then the acyl group content could be calculated from the UV absorbance data and the results were in agreement with those calculated from the data of elemental analysis.

关键词

Keywords

references

Views

161

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Hybrid FC/ZnO materials prepared by RF sputtering and their basic properties

Thermodynamic performance of tower-type solar-assisted supercritical compression CO2 energy storage system

Zn-doped PdO/ZrO2 with rich oxygen vacancies for the synthesis of diphenyl carbonate from CO2 and phenol

Thermo-gas-elastic coupling performance analysis of high-speed and high-temperature foil face seals

Progress in research of selective oxidation of low carbon polyols over nano-Au catalysts with precise electronic effect regulation

Related Author

ZHANG Yuhui

QI Hongjin

Related Institution

青岛大学化学化工学院

东华大学生态纺织教育部重点实验室

五邑大学纺织服装系

⁰