Synthesis and characterization of block copolymers of poly(silane arylacetylene) and poly(siloxane arylacetylene)

WANG Qiang, YANG Jianhui, YUAN Qiaolong, HUANG Farong, DU Lei   

  1. Key Laboratory for Specially Functional Polymeric Materials and Related Technology of Ministry of Education (East China University of Science and Technology), Shanghai 200237, China
  • Received:2014-03-10 Revised:2014-05-09 Online:2014-10-05 Published:2014-05-21
  • Supported by:

    supported by Shanghai Leading Academic Discipline Project(B502).

Abstract: A series of block copolymers of poly(silane arylacetylene) and poly(siloxane arylacetylene) (SiO-b-PSA) were synthesized by the condensation reactions of m-diethynylbenzene magnesium reagents with various a,w-bis(chloro)dimethylsiloxanes. Carbon fiber reinforced composites were prepared through compression molding. The structures and properties of the resins and composites were characterized by FT-IR, 1H NMR, GPC, DSC, TGA and mechanical tests. The copolymers had good heat resistance and toughness. The copolymers also showed excellent processability that could be cured at below 200℃. The cured resins possessed high thermal and thermooxidative stability. Their thermo-decomposition occurred at above 513℃ in N2. Impact strength of the composites arrived at as high as(30.92±0.44) kg·m-2.

Key words: Si-containing arylacetylene resin, siloxane-arylacetylene resin, block copolymer, high temperature polymer, composites, polymerization, chemical reaction

CLC Number: 

  • TQ323.1
[1] Itoh M, Mitsuzuka M, Iwata K, Inoue K. A novel synthesis and extremely high thermal stability of poly[(phenylsilylene)- ethynylene-1,3- phenyleneethynylene][J]. Macromolecules, 1994, 27: 7917-7919
[2] Itoh M, Inoue K, Iwata K, Mitsuzuka M, kakigano T. New highly heat-resistant polymers containing silicon: poly(silyleneethynylene- phenyleneethynylene)s [J].Macromolecules, 1997, 30: 694-701
[3] Yan Hao(严浩), Qi Huimin(齐会民), Huang Farong(黄发荣). Synthesis and properties of novel Si-containing arylacetylene resin [J]. Petrochemical Technology(石油化工), 2004, 33(9): 880-884
[4] Zhang L L, Gao F, Wang C F, Zhang J, Huang F R, Du L. Synthesis and characterization of poly[(methylsilyleneethynylenephenyle- neethynylene)-co-(dimethylsilyleneethynylene phenyleneethyny- lene)]s [J]. Chinese Journal of Polymer Science, 2010, 28(2): 199-207
[5] Jiang Z Y, Zhou Y, Huang F R, Du L. Characterization of modified silicon-containing arylacteylene resin with POSS functionality[J]. Chinese Journal of Polymer Science, 2011, 29(6): 726-731
[6] Wang C F, Huang F R, Jiang Y , Li J F, Zhou Y, Du L. Oxidation behavior of carbon materials derived from a carborane- and silicon-incorporated polymer [J]. Ceramics International, 2012, 38(4): 3081-3088
[7] Deng Lianli(邓莲丽), Shen Minmin(沈敏敏), Yu Jing(于静), Wu Kun(吴昆), Cen Xueyang(岑学杨), Ha Chengyong(哈成勇). Preparation and flame retardancy of siloxane modified epoxy resins based on acrylic acid rosin[J]. CIESC Journal(化工学报), 2012, 63(1): 307-313
[8] Wohl C J, Atkins B M, Belcher M A, Connell J W. Synthesis, characterization, topographical modification, and surface properties of copoly (imide siloxane)s[J]. High Performance Polymers, 2012, 24(1): 40-49
[9] Liu Yanbing(刘衍兵), Guo Kangkang(郭康康), Qi Huimin(齐会民), Huang Farong(黄发荣), Du Lei(杜磊). Thermal stability of blends of polysilane and silicon-containing arylacetylene resin[J]. New Chemical Materials(化工新型材料), 2010, 38(4): 84-87, 106
[10] Gao F, Zhang L L, Tang L M, Zhang J, Zhou Y, Huang F R, Du L. Synthesis and properties of arylacetylene resins with siloxane units[J]. Bulletin of the Korean Chemical Society, 2010, 31(4): 976-980
[11] Gao F, Zhang L L, Huang F R, Du L. Investigation on poly[(methylsilylene ethynylene phenylene ethynylene)-co- (tetramethyldisiloxane ethynylene phenylene ethynylene)][J]. Chinese Chemical Letter, 2010, 21: 738-742
[12] Gao F, Zhang L L, Zhou Y, Huang F R, Du L. Synthesis and characterization of poly[(methylsilyleneethynylenephenyleneeth- ynylene)s -co-decamethylpentasiloxane] [J]. Journal of Macromolecular Science: Part A, 2010, 47(8): 861-866
[13] Gao F, Zhang L L, Tang L M, Huang F R, Du L. Synthesis and characterization of poly(tetramethyldisiloxane-ethynylenephenyle- neethynylene) resins[J]. Journal of Polymer Research, 2011, 18(2): 163-169
[14] Gao Fei(高飞), Wang Fan(王帆), Zhang Lingling(张玲玲), Tang Lemin(汤乐旻), Huang Farong(黄发荣), Du Lei(杜磊), Li Zhongping(李仲平). Synthesis and characterization of siloxane-containing arylactylene resin[J]. Journal of Wuhan University of Technology (武汉理工大学学报), 2009, 31(21): 9-12
[15] Gao F, Huang F R, Tang L M, Du L. Synthesis and characterization of poly(multidimethylsiloxane-1,4- ethynylenephenyleneethynylene)s [J]. Polymer Journal, 2011, 43( 2):136-140
[16] Mirskov R G, Rakhlin V I, Voronkov M G, Gendin D V. Synthesis of 1,1,5,5-tetramethyl-3,3-diorganyltrisiloxanes[J]. Russian Journal of General Chemistry, 2003, 73(1):157
[17] Teng C J, Weber W P, Cai G. Anionic and cationic ring-opening polymerization of 2,2,4,4,6,6-hexamethyl-8,8- divinylcyclotetrasilo- xane [J]. Macromolecules, 2003, 36(14): 5126-5130
[18] Yoshino K, Kawamata A, Uchida H, Kabe Y. A convenient synthesis of α,ω-difunctionalized linear dimethylsiloxanes with definite chain lengths[J]. Chemical Letter, 1990, 19(11): 2133-2136
[19] Manoj K K, Teddy M K. The effects of concentration dilution of cross-linkable diacetylenes on the plasticity of poly(m-carborane- disiloxane-diacetylene)s [J]. Journal of Materials Chemical, 2003, 13: 1652-1656
[20] Chi Tie(池铁), Qi Huimin(齐会民), Huang Farong(黄发荣), Du Lei(杜磊). Thermal oxiadative degradation kinetics of silicon-arylactylene-containing resin[J]. Fiber Reinforced Plastics/ Composites (玻璃钢/复合材料), 2013, 2: 34-38
[1] WANG Fayang, DU Jun, DAI Lu, WU Haichao, WANG Youyong, SONG Yongming. Effect of divinylbenzene-assisted maleic anhydride grafted poly(lactic acid) on properties of microcrystalline cellulose/poly(lactic acid) composites [J]. CIESC Journal, 2019, 70(1): 327-335.
[2] ZHOU Sunxi, ZHANG Xuelai, LIU Sheng, CHEN Qiyang, XU Xiaofeng, WANG Yinghui. Preparation and properties of decyl alcohol-palmitic acid/expanded graphite low temperature composite phase change material [J]. CIESC Journal, 2019, 70(1): 290-297.
[3] XIANG Wenjun, ZHU Zhaoju, LIU Dan, ZHOU Lüshan. Molecular dynamics simulations core-shell self-assembly from amphiphilic polymer and hydrophobic nanoparticle [J]. CIESC Journal, 2019, 70(1): 345-354.
[4] JIA Shangning, CHANG Juanjuan, LI Ningbo, QIAO Jie. Synthesis of magnetic nanoparticles with core-shell structure and its drug loading properties [J]. CIESC Journal, 2018, 69(S1): 170-175.
[5] ZHENG Lifang, WANG Zhaozhong, XIE Yajie, YUE Lina, WANG Li. Kinetic study on thermal decomposition of GFRP under γ irradiation [J]. CIESC Journal, 2018, 69(S1): 161-169.
[6] ZHANG Liang, SHI Zhongke. Experimental exploration of passive energy storage device with phase change materials for vehicle [J]. CIESC Journal, 2018, 69(S1): 176-181.
[7] TANG Erjun, YAO Mengmeng, GUO Xiaofeng, WANG Ruihong, LIU Shaojie, GAO Hao. Film formation for aqueous epoxy acrylate latex coatings [J]. CIESC Journal, 2018, 69(S1): 143-147.
[8] CUI Lingna, LIU Yuejun. Synthesis process optimization and degradation properties of PLA/PBAu block copolymer [J]. CIESC Journal, 2018, 69(9): 4075-4082.
[9] HOU Zhenzhong, PENG Longgui, LI Ying, LU Hai, LU Ya, XIE Xiaoqin. Interfacial self-assembly synthesis and electrochemical capacitance of hierarchical porous polypyrrole films [J]. CIESC Journal, 2018, 69(9): 4121-4128.
[10] LI Yajuan, ZHAO Chuanqi, YANG Yuesuo, WANG Yuanyuan, SONG Xiaoming. Mechanism and model of dynamic adsorption of glyphosate contaminated water on graphene-based iron oxide composite [J]. CIESC Journal, 2018, 69(9): 3944-3953.
[11] LI Peijie, YANG Bo, LI Hongguang. Association rules based conditional state fuzzy Petri nets with applications in fault diagnosis [J]. CIESC Journal, 2018, 69(8): 3517-3527.
[12] TIAN Haifeng, YAO Lu, GAO Jialiang, ZHA Fei, GUO Xiaojun. Effects of silylation and organic weak alkali modified Mo/HZSM-5 on catalytic performance in non-oxidative aromatization of methane reaction [J]. CIESC Journal, 2018, 69(7): 3009-3017.
[13] HUANG Pan, LIU Zhen, SHAO Yunqi, DENG Shifeng, LIU Boping. Influences of organic additives on inhibiting by-products in zinc-catalyzed synthesis of alkynylsilane [J]. CIESC Journal, 2018, 69(7): 2993-3000.
[14] WU Nie, WAN Liying, LI Aimei, XIAO Chunping. Shape memory properties of mesogen-jacketed liquid crystalline polymers based on vinylterephthalic acid [J]. CIESC Journal, 2018, 69(5): 2282-2289.
[15] ZHANG Ao, YANG Haicun, MA Wenzhong, LI Yuxue, GONG Fanghong, TAO Guoliang, LIU Chunlin. Preparation of attapulgite/polystyrene hybrid particles via simultaneous reverse and normal initiation atom transfer radical polymerization [J]. CIESC Journal, 2018, 69(5): 2299-2308.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!