分级多孔聚吡咯膜的界面自组装合成与电化学电容性

doi:10.11949/j.issn.0438-1157.20180347

摘要/Abstract

摘要：

通过界面自组装聚合，在长链表面活性剂OP10的辅助下成功制备了分级多孔结构聚吡咯膜。对所得聚吡咯的分子结构、微观形貌和电化学性能分别进行了表征和研究。结果表明：界面聚合中引入OP10对聚吡咯的分子结构并没有影响，但对其微观形貌却具有重要作用。当OP10的用量优化为0.02 g时，聚吡咯可自组装形成分级多孔结构，既有纳米孔（约100 nm），也有亚微米孔（200~1000 nm）和微米孔（1~3.5 μm）。由于相对较高的活性表面积和总孔体积，分级多孔聚吡咯作为电极材料最大比电容可达357 F·g^-1，比相同条件下传统界面法制备的聚吡咯高70%以上。此外，2000次充放电循环后该材料仍保持初始比电容的87.6%，表明其优异的循环稳定性。

关键词: 界面聚合, 聚吡咯, 表面活性剂, 显微结构, 自组装, 电化学

Abstract:

Hierarchical porous polypyrrole films have been successfully prepared by interfacial self-assembly polymerization with assistance of the long-chain surfactant OP10. The molecular structure, micromorphology and electrochemical performance of obtained polypyrrole were characterized. The results showed that introducing OP10 into interfacial polymerization had no effect on the molecular structure of obtained polypyrrole but a significant impact on its micromorphology. When the dosage of OP10 was optimized at 0.02 g, polypyrrole could self-assemble to form a hierarchical porous structure including nanopores (~100 nm), submicron pores (200-1000 nm) and micron pores (1-3.5 μm). Because of relatively larger active surface area and higher total pore volume, hierarchical porous polypyrrole, as the electrode material, possessed a maximum specific capacitance up to 357 F·g^-1 which is 70% higher than that prepared by traditional interfacial synthesis at the same conditions. Furthermore, 87.6% of the initial specific capacitance was still retained even after 2000 charge-discharge cycles, indicating the excellent cycling stability of the prepared polypyrrole.

Key words: interfacial polymerization, polypyrrole, surfactants, microstructure, self-assembly, electrochemistry

中图分类号:

TQ630.1
TB34

后振中, 彭龙贵, 李颖, 卢海, 陆亚, 谢晓琴. 分级多孔聚吡咯膜的界面自组装合成与电化学电容性[J]. 化工学报, 2018, 69(9): 4121-4128.

HOU Zhenzhong, PENG Longgui, LI Ying, LU Hai, LU Ya, XIE Xiaoqin. Interfacial self-assembly synthesis and electrochemical capacitance of hierarchical porous polypyrrole films[J]. CIESC Journal, 2018, 69(9): 4121-4128.

参考文献 42

[1]	SNOOK G A, KAO P, BEST A S. Conducting polymer based supercapacitor devices and electrodes[J]. J. Power Sources, 2011, 196(1):1-12.
[2]	WAN G, ZHANG L, ZHANG J. A review of electrode materials for electrochemical supercapacitors[J]. Chem. Soc. Rev., 2012, 43(18):797-828.
[3]	HUGHES M, CHEN G Z, SHAFFER M S P, et al. Controlling the nanostructure of electrochemically grown nanoporous composites of carbon nanotubes and conducting polymers[J]. Compos. Sci. Technol., 2004, 64(15):2325-2331.
[4]	SHARMA R K, RASTOGI A C, DESU S B. Manganese oxide embedded polypyrrole nanocomposites for electrochemical supercapacitor[J]. Electrochim. Acta, 2008, 53(26):7690-7695.
[5]	SNOOK G A, BEST A S. Co-deposition of conducting polymers in a room temperatureionic liquid[J]. J. Mater. Chem., 2009, 19(24):4248-4254.
[6]	AFZAL A, ABUILAIWI F A, HABIB A, et al. Polypyrrole/carbon nanotube supercapacitors:technological advances and challenges[J]. J. Power Sources, 2017, 352:174-186.
[7]	杜伟, 鞠翔宇, 王美丽, 等. 石墨烯/聚吡咯导电复合材料超级电容器电极的制备研究[J]. 功能材料, 2017, 48(1):1034-1037. DU W, JU X Y, WANG M L, et al. Study on the preparation of graphene/polypyrrole conductive composites supercapacitor electrode[J]. J. Funct. Mater., 2017, 48(1):1034-1037.
[8]	LEE H, CHO M S, KIM I H, et al. RuOx/polypyrrole nanocomposite electrode for electrochemical capacitors[J]. Synth. Met., 2010, 160(9/10):1055-1059.
[9]	WEI H, HE C, LIU J, et al. Electropolymerized polypyrrole nanocomposites with cobalt oxide coated on carbon paper for electrochemical energy storage[J]. Polymer, 2015, 67(1):192-199.
[10]	ZHANG J, LIU Y, GUAN H, et al. Decoration of nickel hydroxide nanoparticles onto polypyrrole nanotubes with enhanced electrochemical performance for supercapacitors[J]. J. Alloys Compd., 2017, 721:731-740.
[11]	SHARMA R K, RASTOGI A C, DESU S B. Pulse polymerized polypyrrole electrodes for high energy density electrochemical supercapacitor[J]. Electrochem. Commun., 2008, 10(2):268-272.
[12]	CHEN S, LIU H, WANG Y, et al. Electrochemical capacitance of spherical nanoparticles formed by electrodeposition of intrinsic polypyrrole onto Au electrode[J]. Electrochim. Acta, 2017, 232:72-79.
[13]	SHI Y, PAN L J, LIU B R, et al. Nanostructured conductive polypyrrole hydrogels as high-performance, flexible supercapacitor electrodes[J]. J. Mater. Chem. A, 2014, 2(17):6086-6091.
[14]	王亮, 丁春梅, 朱英, 等. 超疏水导电聚苯胺的界面聚合[J]. 高等学校化学学报, 2012, 33(6):1355-1359. WANG L, DING C M, ZHU Y, et al. Superhydrophobic conducting polyaniline prepared via interfacial polymerization[J]. Chem. J. Chinese Univ., 2012, 33(6):1355-1359.
[15]	陈祥凤, 姜均涛. 界面聚合法制备管状聚苯胺/聚苯胺包覆镍纳米复合材料及其电磁特性[J]. 材料导报, 2016, 30(S2):45-48. CHEN X F, JIANG J T. Synthesis of tube-polyaniline/polyaniline coated Ni nanoparticle composite by a simple interface polarization process and their electromagnetic properties[J]. Mater. Rev., 2016, 30 (S2):45-48.
[16]	DALLAS P, GEORGAKILAS V. Interfacial polymerization of conductive polymers:generation of polymeric nanostructures in a 2-D space[J]. Adv. Colloid Interface Sci., 2015, 224:46-61.
[17]	BORA C, DOLUI S K. Fabrication of polypyrrole/graphene oxide nanocomposites by liquid/liquid interfacial polymerization and evaluation of their optical, electrical and electrochemical properties[J]. Polymer, 2012, 53(4):923-932.
[18]	HOU L, YUAN C, LI D, et al. Water/ionic liquid/organic three-phase interfacial synthesis of coral-like polypyrrole toward enhanced electrochemical capacitance[J]. Electrochim. Acta, 2011, 56(17):6049-6054.
[19]	朱英, 万梅香, 江雷. 聚苯胺微/纳米结构及其应用[J]. 高分子通报, 2011, (10):15-32. ZHU Y, WAN M X, JIANG L. Self-asseblied polyaniline micro/nanostructures and their applications[J]. Polym. Bull., 2011, (10):15-32.
[20]	PRATHAP M U, THAKUR B, SAWANT S N, et al. Synthesis of mesostructured polyaniline using mixed surfactants, anionic sodium dodecylsulfate and non-ionic polymers and their applications in H2O2 and glucose sensing[J]. Colloids Surf. B, 2012, 89(1):108-115.
[21]	JAIN D, HASHMI S A, KAUR A. Surfactant assisted polyaniline nanofibres-reduced graphene oxide (SPG) composite as electrode material for supercapacitors with high rate performance[J]. Electrochim. Acta, 2016, 222:570-579.
[22]	后振中, 杨庆浩, 刘俊. 界面聚合自组装合成三维多孔网络状聚邻甲基苯胺[J]. 功能高分子学报, 2016, 29(3):318-322. HOU Z Z, YANG Q H, LIU J. Self-assembly synthesis of 3D porous network poly(o-toluidine) via interfacial polymerization[J]. J. Func. Polym., 2016, 29(3):318-322.
[23]	LIU P, WANG X, LI H. Preparation of carboxylated carbon nanotubes/polypyrrole composite hollow microspheres via chemical oxidative interfacial polymerization and their electrochemical performance[J]. Synth. Met., 2013, 181(5):72-78.
[24]	LEI W, HE P, WANG Y, et al. Soft template interfacial growth of novel ultralong polypyrrole nanowires for electrochemical energy storage[J]. Electrochim. Acta, 2014, 132(3):112-117.
[25]	黄天柱, 杨庆浩, 屠钟艺, 等. 分形结构聚吡咯膜的界面聚合与电容特性表征[J]. 高分子材料科学与工程, 2015, 2(31):41-45. HUANG T Z, YANG Q H, TU Z Y, et al. Interfacial polymerization and capacitive properties of multifractal dimensions polypyrrole film[J]. Highpolymer Mater. Sci. & Eng., 2015, 2(31):41-45.
[26]	LIU C, HAN G, CHANG Y, et al. High-performance supercapacitors based on the reduced graphene oxide hydrogels modified by trace amounts of benzenediols[J]. Chem. Eng. J., 2017, 328:25-34.
[27]	LIU J, WAN M X. Synthesis, characterization and electrical properties of microtubules of polypyrrole synthesized by a template-free method[J]. J. Mater. Chem., 2001, 11(2):404-407.
[28]	SHEN M, HAN Y, LIN X, et al. Preparation and electrochemical performances of porous polypyrrole film by interfacial polymerization[J]. J. Appl. Polym. Sci., 2013, 127(4):2938-2944.
[29]	?IRI?-MARJANOVI? G, MENTUS S, PAŠTI I, et al. Synthesis, characterization, and electrochemistry of nanotubular polypyrrole and polypyrrole-derived carbon nanotubes[J]. J. Phys. Chem. C, 2014, 118(27):14770-14784.
[30]	RANA U, CHAKRABARTI K, MALIK S. In situ preparation of fluorescent polyaniline nanotubes doped with perylene tetracarboxylic acids[J]. J. Mater. Chem., 2011, 21(30):11098-11100.
[31]	MOLINA J, ZILLE A, FERNANDEZ J, et al. Conducting fabrics of polyester coated with polypyrrole and doped with graphene oxide[J]. Synth. Met., 2015, 204:110-121.
[32]	WANG Z L, HE X J, YE S H, et al. Design of polypyrrole/polyaniline double-walled nanotube arrays for electrochemical energy storage[J]. ACS Appl. Mater. Interfaces, 2014, 6(1):642-647.
[33]	GUPTA S. Hydrogen bubble-assisted syntheses of polypyrrole micro/nanostructures using electrochemistry:structural and physical property characterization[J]. J. Raman Spectrosc, 2008, 39(10):1343-1355.
[34]	BAI N, XU Z, TIAN Y, et al. Tailorable polypyrrole nanofilms with exceptional electrochemical performance for all-solid-state flexible supercapacitors[J]. Electrochim. Acta, 2017, 249:360-368.
[35]	WANG J, XU Y L, YAN F, et al. Template-free prepared micro/nanostructured polypyrrole with ultrafast charging/discharging rate and long cycle life[J]. J. Power Sources, 2011, 196(4):2373-2379.
[36]	马国富, 牟晶晶, 张稚国, 等. 聚吡咯/海藻酸钠纳米球的制备及其应用于高性能超级电容器[J]. 物理化学学报, 2013, 29(11):2385-2391. MA G F, MU J J, ZHANG Z G, et al. Preparation of polypyrrole/sodium alginate nanospheres and their application for high-performance supercapacitors[J]. Acta Phys. -Chim. Sin., 2013, 29(11):2385-2391.
[37]	RAMYA R, SIVASUBRAMANIAN R, SANGARANARAYANAN M V. Conducting polymers-based electrochemical supercapacitors-progress and prospects[J]. Electrochim. Acta, 2013, 101(7):109-129.
[38]	ZHANG F, XIAO F, DONG Z H, et al. Synthesis of polypyrrole wrapped graphene hydrogels composites as supercapacitor electrodes[J]. Electrochim. Acta, 2013, 114:125-132.
[39]	LI Y Z, ZHAO X, XU Q, et al. Facile preparation and enhanced capacitance of the polyaniline/sodium alginate nanofiber network for supercapacitors[J]. Langmuir, 2011, 27(10):6458-6463.
[40]	YANG Q H, HOU Z Z, HUANG T Z. Self-assembled polypyrrole film by interfacial polymerization for supercapacitor applications[J]. J. Appl. Polym. Sci., 2015, 132(11):41615.
[41]	HOU Z Z, LU H, YANG Q H, et al. Micromorphology-controlled synthesis of polypyrrole films by using binary surfactant of Span80/OP10via interfacial polymerization and their enhanced electrochemical capacitance[J]. Electrochim. Acta, 2018, 265:601-608.
[42]	SHI Y, PENG L, DING Y, et al. Nanostructured conductive polymers for advanced energy storage[J]. Chem. Soc. Rev., 2015, 44(19):6684-6696.